A white emitting copolymer with the polyphenylenevinylene (PPV) structure is obtained via the Stille cross-coupling reaction. Substitution of hydrogen atoms with fluorine atoms on the vinylene units of poly(1,4-dialkoxyphenylenevinylene) shifts the emission from orange-red to blue. White emission is obtained by combining dialkoxyphenylenedifluorovinylene and dialkoxyphenylenevinylene units in proper ratio. The two complementary emitters are obtained separately by Stille polymerization reaction. Then, the two reaction mixtures are combined without purification in different ratios and further reacted in similar experimental conditions. A white luminescent material is obtained using 99/1 mixing ratio. OLED devices fabricated with this copolymer shows near-white emission with CIE (0.30, 0.40) and excellent stability in the range 10e200 cd/m2.

A white emitting poly(phenylenevinylene)

FARINOLA, Gianluca Maria
2014

Abstract

A white emitting copolymer with the polyphenylenevinylene (PPV) structure is obtained via the Stille cross-coupling reaction. Substitution of hydrogen atoms with fluorine atoms on the vinylene units of poly(1,4-dialkoxyphenylenevinylene) shifts the emission from orange-red to blue. White emission is obtained by combining dialkoxyphenylenedifluorovinylene and dialkoxyphenylenevinylene units in proper ratio. The two complementary emitters are obtained separately by Stille polymerization reaction. Then, the two reaction mixtures are combined without purification in different ratios and further reacted in similar experimental conditions. A white luminescent material is obtained using 99/1 mixing ratio. OLED devices fabricated with this copolymer shows near-white emission with CIE (0.30, 0.40) and excellent stability in the range 10e200 cd/m2.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11586/39596
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? 7
social impact