Hysteresis behaviour of the current–voltage characteristics collected on spin coated synthetic eumelanin layer embedded in the Au/eumelanin/ITO/glass structure is shown. The effect has been observed under dark both in air and vacuum environment and its magnitude has been found related to the eumelanin hydration state. Moreover, in vacuum and under white light illumination, enhancement of the hysteresis loop area respect to those collected under dark has been observed. Space charge storage and charge trapping/detrapping as possible mechanisms responsible of the observed current–voltage behaviour are discussed. Preliminary experimental results have evidenced the possible integration of eumelanin layers in electro-optical charge storage based memory devices.

Hysteresis-type current-voltage characteristics in Au/eumelanin/ITO/glass structure: towards melanin based memory devices

LIGONZO, Teresa;FARINOLA, Gianluca Maria;
2010

Abstract

Hysteresis behaviour of the current–voltage characteristics collected on spin coated synthetic eumelanin layer embedded in the Au/eumelanin/ITO/glass structure is shown. The effect has been observed under dark both in air and vacuum environment and its magnitude has been found related to the eumelanin hydration state. Moreover, in vacuum and under white light illumination, enhancement of the hysteresis loop area respect to those collected under dark has been observed. Space charge storage and charge trapping/detrapping as possible mechanisms responsible of the observed current–voltage behaviour are discussed. Preliminary experimental results have evidenced the possible integration of eumelanin layers in electro-optical charge storage based memory devices.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11586/15248
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 54
  • ???jsp.display-item.citation.isi??? 51
social impact