We describe a possible correlation between the bias voltage applied to the substrate during the growth of CsI photocathodes and the variation of quantum efficiency (QE) after one day exposure to humid air. It was found that fresh samples are much less sensitive to humid air when a high negative bias voltage was applied during film growth. A model based on surface film interaction with water molecules is presented for the observed effect. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) measurements have been performed to examine, respectively, the bulk structure and the surface of fresh and exposed CsI samples. Also reported are transmittance measurements for fresh and aged CsI samples in the wavelength range 190-850 nm. (C) 2002 Elsevier Science B.V. All rights reserved.

Influence of bias voltage on the stability of CsI photocathodes exposed to air

CIOFFI, NICOLA;VALENTINI, Antonio
2002-01-01

Abstract

We describe a possible correlation between the bias voltage applied to the substrate during the growth of CsI photocathodes and the variation of quantum efficiency (QE) after one day exposure to humid air. It was found that fresh samples are much less sensitive to humid air when a high negative bias voltage was applied during film growth. A model based on surface film interaction with water molecules is presented for the observed effect. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) measurements have been performed to examine, respectively, the bulk structure and the surface of fresh and exposed CsI samples. Also reported are transmittance measurements for fresh and aged CsI samples in the wavelength range 190-850 nm. (C) 2002 Elsevier Science B.V. All rights reserved.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11586/126871
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 25
  • ???jsp.display-item.citation.isi??? 21
social impact