In this paper a study of Multi Wall Carbon Nanotube films deposited at low temperature by means of a spray technique on different substrates is presented. Nanodispersion of nanotube powder in a non-polar 1,2-dichloroethane solvent was used as starting solution. Electron Microscopy in Scanning and Transmission modes were used in order to verify the morphological properties of the deposited films. Visible light detectors were prepared spraying Multi Wall Carbon Nanotubes on silicon substrates with different layouts. In some detectors the nanotubes were covered by an Indium Tin Oxide (ITO) layer. Electrical measurements, both in dark and under light irradiation, were performed and Current-Voltage characteristics are reported. The Indium Tin Oxide coating effect on the photoconductivity yield is presented and discussed along with device ageing test, resulting in a very good photoconduction and stability over four months.
Radiation detectors based on Multiwall Carbon Nanotubes deposited by a spray technique
VALENTINI, Antonio;DITARANTO, NICOLETTA;CIOFFI, NICOLA;
2013-01-01
Abstract
In this paper a study of Multi Wall Carbon Nanotube films deposited at low temperature by means of a spray technique on different substrates is presented. Nanodispersion of nanotube powder in a non-polar 1,2-dichloroethane solvent was used as starting solution. Electron Microscopy in Scanning and Transmission modes were used in order to verify the morphological properties of the deposited films. Visible light detectors were prepared spraying Multi Wall Carbon Nanotubes on silicon substrates with different layouts. In some detectors the nanotubes were covered by an Indium Tin Oxide (ITO) layer. Electrical measurements, both in dark and under light irradiation, were performed and Current-Voltage characteristics are reported. The Indium Tin Oxide coating effect on the photoconductivity yield is presented and discussed along with device ageing test, resulting in a very good photoconduction and stability over four months.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.