Herein, we explored the modification of wheat straw biochar with chitosan, quaternary ammonium salt, and lanthanum for enhanced phosphate removal in environmentally relevant conditions. Specifically, a new amine protected cross-linking method was utilized to modify the absorbent material for maximum adsorption capacity, reaching 109 ± 4 mg P g−1. The high phosphate removal performance of the composite was not significantly affected in a broad range of temperature (15–45 °C) and pH (2.5–7). 30 min allowed reaching a 100% adsorption equilibrium for 100 mg P L−1, and 93% for 25 mg P L−1, thus, significantly reducing the treatment time compared to previous reports. The highest partition coefficient 172.1 mg g−1 μM−1 was obtained at a concentration of 25 mg L−1, and the phosphorus removal rate was as high as 99.98%, indicating La/GTB have great adsorption performance at low phosphate concentration. The adsorption mechanisms of the composite are extensively described, where electrostatic interaction, ligand exchange, and Lewis acid-base interaction contribute to the process. All of the above-mentioned advantages make the prepared composite of great interest for the development of materials for on-site phosphate removal.
Modified biochar for phosphate adsorption in environmentally relevant conditions
Grattieri M.;
2020-01-01
Abstract
Herein, we explored the modification of wheat straw biochar with chitosan, quaternary ammonium salt, and lanthanum for enhanced phosphate removal in environmentally relevant conditions. Specifically, a new amine protected cross-linking method was utilized to modify the absorbent material for maximum adsorption capacity, reaching 109 ± 4 mg P g−1. The high phosphate removal performance of the composite was not significantly affected in a broad range of temperature (15–45 °C) and pH (2.5–7). 30 min allowed reaching a 100% adsorption equilibrium for 100 mg P L−1, and 93% for 25 mg P L−1, thus, significantly reducing the treatment time compared to previous reports. The highest partition coefficient 172.1 mg g−1 μM−1 was obtained at a concentration of 25 mg L−1, and the phosphorus removal rate was as high as 99.98%, indicating La/GTB have great adsorption performance at low phosphate concentration. The adsorption mechanisms of the composite are extensively described, where electrostatic interaction, ligand exchange, and Lewis acid-base interaction contribute to the process. All of the above-mentioned advantages make the prepared composite of great interest for the development of materials for on-site phosphate removal.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.