The mechanical failure of a dental implant is clinically related to a prosthetic overload dissipated on the fixture/abutment complex. the aim of this investigation was to evaluate the fracture srenght of two vs three narrow-diameter dental implants (Group I) and screw-retained bars on three narrow-diameter dental implants (Group II) were tested under a static fracture loading. A total of 20 specimens, 10 for each group were evaluated. The fracture loading point was significatively higher in Group I (p<0.05). The experimental groups reported high levels of fracture strength under loading that encourages the clinical application of screw-retained bars supported by multiple narrow-diameter implants.
IN VITRO INTERFACE CHANGES OF TWO VS THREE NARROW-DIAMETER DENTAL IMPLANTS FOR SCREW-RETAINED BAR UNDER FATIGUE LOADING TEST
F. INCHINGOLO;
2019-01-01
Abstract
The mechanical failure of a dental implant is clinically related to a prosthetic overload dissipated on the fixture/abutment complex. the aim of this investigation was to evaluate the fracture srenght of two vs three narrow-diameter dental implants (Group I) and screw-retained bars on three narrow-diameter dental implants (Group II) were tested under a static fracture loading. A total of 20 specimens, 10 for each group were evaluated. The fracture loading point was significatively higher in Group I (p<0.05). The experimental groups reported high levels of fracture strength under loading that encourages the clinical application of screw-retained bars supported by multiple narrow-diameter implants.File | Dimensione | Formato | |
---|---|---|---|
IN VITRO INTERFACE CHANGES OF TWO VS THREENARROW-DIAMETER DENTAL IMPLANTS FOR SCREW-RETAINED BAR UNDER FATIGUE LOADING TEST.pdf
non disponibili
Tipologia:
Documento in Versione Editoriale
Licenza:
NON PUBBLICO - Accesso privato/ristretto
Dimensione
712.66 kB
Formato
Adobe PDF
|
712.66 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.