IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishWe exploit TiO2 surface functionalization as a tool to induce the crystallization process of CH3NH3PbI3−xClx perovskite thin films resulting in a reduction of the degree of orientation of the (110) crystallographic planes. Notably, the variation of the film crystalline orientational order does not affect the photovoltaic performances of the perovskite-based devices, whose efficiency remains mostly unchanged. Our findings suggest that other factors are more significant in determining the device efficiency, such as the non-homogenous coverage of the TiO2 surface causing charge recombination at the organic/TiO2 interface, defect distribution on the perovskite bulk and at the interfaces, and transport in the organic or TiO2 layer. This observation represents a step towards the comprehension of the perovskite film peculiarities influencing the photovoltaic efficiency for high performance devices.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
| Titolo: | Implications of TiO2surface functionalization on polycrystalline mixed halide perovskite films and photovoltaic devices | |
| Autori: | ||
| Data di pubblicazione: | 2015 | |
| Rivista: | ||
| Abstract: | We exploit TiO2 surface functionalization as a tool to induce the crystallization process of CH3NH3PbI3−xClx perovskite thin films resulting in a reduction of the degree of orientation of the (110) crystallographic planes. Notably, the variation of the film crystalline orientational order does not affect the photovoltaic performances of the perovskite-based devices, whose efficiency remains mostly unchanged. Our findings suggest that other factors are more significant in determining the device efficiency, such as the non-homogenous coverage of the TiO2 surface causing charge recombination at the organic/TiO2 interface, defect distribution on the perovskite bulk and at the interfaces, and transport in the organic or TiO2 layer. This observation represents a step towards the comprehension of the perovskite film peculiarities influencing the photovoltaic efficiency for high performance devices. | |
| Handle: | http://hdl.handle.net/11586/262260 | |
| Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
Copyright © 2021